Model Number: pipe flanges gasket NXB
Brand Name: TENSION
Key Specifications/Special Features:
Non asbestos oil resistant gasket sealing sheetfor marine pipe flanges:Non-asbestos jointing sheets are made of special no-asbestos heat-resisting fiber, heat-resisting packing material and special nature or NBR rubber compound heating and compression molding itNon-asbestos rubber sheet series include: NXB200, NXB300, NXB350Uses: used for the equipment in water, steam and used as sealing material in the joints of pipelineWorking pressure: 1.5-8.0 MPa
Working temperature: 150 to 450°C
Oil-resistance non-asbestos rubber sheet series include:NNY150, NNY250, NNY300, NNY350
Uses: mainly used as the aviation liquid the motive's kerosene, lubricant, the fuel oil and cold air system to join together the seal completely of place the sealing gasket material
Working pressure: 7.0 to 12MPa
Working temperature: 150 to 450°C
Available sizes:Thickness: 0.5 to 5mm
Sizes:1300 x 1300, 1500 x 2000,1270 x 1270,1270 x 3810, 1500 x 1500, 1500 x 1360, 1500 x 1000 and 1300 x 4050mm
Other size is optional or according to the requirements of customers
At the same time, steel wire net inserted (coated graphite) is available
Packing:in wooden pallet or cases of about 1000 and 2000kg net each
Shipping:7
-20 days after receive 35% advance payment
Item |
NXB200 |
NXB300 |
NXB350 |
NNY150 |
NNY250 |
NNY300 |
NNY350 |
Tensile strength MPa≥ |
5 |
7 |
11 |
8 |
10 |
12 |
15 |
Aging Coefficient ≥ |
0.9 |
|
|
|
|
|
|
Density g/cm g/cm3 |
1.6 2.0 |
1.6 1.8 |
|
|
|
Compressibility % |
12 ± 7 |
|
|
|
|
|
|
Rebound degree |
35 |
40 |
45 |
40 |
45 |
50 |
50 |
Pliability |
No Crack |
|
|
|
|
|
|
Stress-relaxation≤ % |
45 |
45 |
45 |
40 |
40 |
30 |
30 |
Oil sealing |
|
|
|
10 MPa pressure for 30 min |
12 MPa pressure for 30 min |
15MPa pressure for 30 min |
16 MPa pressure for 30 min |
With the temperature |
No leaking |
No leaking |
No leaking |
No leaking |
of 15to 30,.75aviation gasoline for 30 min |
|
|
|
|
With the temperature of 150±2,dipped in No.20 aviation oil for 5h,then taken out and laid for 5min. |
Tensile strength-reducing % |
40 |
30 |
25 |
25 |
Thickness-increasing %≤ |
520 |
520 |
518 |
518 |
Appearance change |
No bubble |
|
|
|
With the temperature |
Tensile strength MPa ≥ |
5 |
6 |
8 |
10 |
of 15 to 30 ,dipped in No.75 aviation oil for 5h,then taken out and laid for 5min. |
Thickness-increasing % |
525 |
525 |
520 |
520 |
|
Pliability |
No Crack |
|
|
|